Influence of the w/c ratio on the hydration process of a magnesium phosphate cement and on its retardation by boric acid - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Cement and Concrete Research Année : 2018

Influence of the w/c ratio on the hydration process of a magnesium phosphate cement and on its retardation by boric acid

Résumé

Magnesium potassium phosphate cements (MKPCs) are prepared using calcined magnesia (MgO) and an acidic solution of potassium dihydrogen phosphate (KH2PO4). Their fast setting and high heat of hydration can be problematic when large volumes of materials are produced. Boric acid (B(OH)(3)) is thus commonly added as a set retarder. This work investigates MKPC hydration in paste (water-to-cement ratio w/c = 1) and its retardation by B(OH)(3). The precipitation of K-struvite (MgKPO4 center dot 6H(2)O) is preceded by that of phosphorosslerite (MgHPO4 center dot 7H(2)O) and Mg2KH(PO4)(2)center dot 15H(2)O. Cattiite (Mg-3(PO4)(2)center dot 22H(2)O), an end-product in diluted suspension (w/c = 100), is not observed. B(OH)3 slows down the formation of hydrates in two ways: (i) by stabilizing in solution the cations that outbalance the negative charges of the polyborates formed at pH above 6, and (ii) through the precipitation of an amorphous mineral containing borate and orthophosphate. The first process occurs both in diluted suspensions and pastes, the second is specific to pastes.
Fichier non déposé

Dates et versions

hal-02008865 , version 1 (06-02-2019)

Identifiants

Citer

Hugo Lahalle, Céline Cau Dit Coumes, Cyrille Mercier, David Lambertin, Céline Cannes, et al.. Influence of the w/c ratio on the hydration process of a magnesium phosphate cement and on its retardation by boric acid. Cement and Concrete Research, 2018, 109, pp.159-174. ⟨10.1016/j.cemconres.2018.04.010⟩. ⟨hal-02008865⟩
78 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More