Evidence of 3D strain gradients associated with tin whisker growth - Archive ouverte HAL
Article Dans Une Revue Scripta Materialia Année : 2018

Evidence of 3D strain gradients associated with tin whisker growth

Résumé

We have used Differential Aperture X-ray Microscopy (DAXM) to measure grain orientations and deviatoric elastic strains in 3D around a tin whisker. The results show strain gradients through the depth of the tin coating, revealing a higher strain deeper in the Sn layer. These higher strains are explained by the volume change occurring during growth of the intermetallic phase Cu6Sn5 at the interface between the Cu substrate and the Sn coating and at grain boundaries between Sn grains.

Domaines

Science des matériaux [cond-mat.mtrl-sci]
Fichier principal
Vignette du fichier
1-s2.0-S1359646217305420-main.pdf (907.32 Ko) Télécharger le fichier
Origine Fichiers éditeurs autorisés sur une archive ouverte

Odile Robach  : Connectez-vous pour contacter le contributeur

https://hal.science/hal-02007991

Soumis le : mardi 5 février 2019-16:59:16

Dernière modification le : mercredi 18 décembre 2024-09:49:14

Archivage à long terme le : lundi 6 mai 2019-17:12:29

Télécharger pour visualiser

Dates et versions

hal-02007991 , version 1 (05-02-2019)

Licence

Paternité - Pas d'utilisation commerciale - Pas de modification

Identifiants

Citer

Johan Hektor, Jean-Baptiste Marijon, Matti Ristinmaa, Stephen Hall, Håkan Hall, et al.. Evidence of 3D strain gradients associated with tin whisker growth. Scripta Materialia, 2018, 144, pp.1-4. ⟨10.1016/j.scriptamat.2017.09.030⟩. ⟨hal-02007991⟩

Exporter

BibTeX XML-TEI Dublin Core DC Terms EndNote DataCite

Collections

CEA UGA CNRS CNAM INAC-SP2M INC-CNRS CEA-DRF IRIG CEA-GRE PIMM SYMMES HESAM IRENAV LAMPA LCPI LABOMAP LISPEN MSMP
110 Consultations
98 Téléchargements

Altmetric

Partager

More