Removal of europium on GMZ bentonite corroded by young cement water at different temperatures

Zhao Sun
  • Fonction : Auteur
Yu-Jun Cui
Wei-Min Ye
  • Fonction : Auteur
  • PersonId : 863451
Dong-Bei Wu
  • Fonction : Auteur

Résumé

After construction of the high-level radioactive waste repository, the bentonite undergoes corrosion of the alkaline solution produced by cement degradation. Young cement water-YCW was employed to carry out the corrosion experiments on compacted GMZ bentonite specimens. Then the removal of europium (Eu(III)) onto corroded GMZ bentonite was studied by batch experiments. The results show the YCW corroded GMZ bentonite is still an effective adsorbent. The adsorption reaction of Eu(III) on corroded GMZ bentonite is endothermic. It can be described by Langmuir isotherm model well. The bentonite corroded at higher temperature shows more stable sorption property.
Fichier non déposé

Dates et versions

hal-01982160 , version 1 (15-01-2019)

Identifiants

Citer

Zhao Sun, Yong-Gui Chen, Yu-Jun Cui, Wei-Min Ye, Dong-Bei Wu. Removal of europium on GMZ bentonite corroded by young cement water at different temperatures. Journal of Radioanalytical and Nuclear Chemistry, 2018, 318 (2), pp.1297-1305. ⟨10.1007/s10967-018-6175-8⟩. ⟨hal-01982160⟩
38 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More