Dynamic rheological behavior of poly(ether ketone ketone) from solid state to melt state

Résumé

High performance thermoplastic poly(ether ketone ketone) (PEKK) polymers with various meta phenyl links ratio were investigated by dynamical mechanical analysis. Analyses were carried out in a wide range of temperature from solid state (torsion rectangular mode) to the melt state (torsion parallel plates mode) as function of thermal history and environmental conditions. In the solid state, this study was focused on the secondary relaxations in the vitreous state. A complementary investigation conducted with different poly(aryl ether ketones) allowed us to propose a molecular interpretation of PEKK sub-vitreous relaxations. In the molten state, storage modulus (G0), loss modulus (G00), storage viscosity (h0), and loss viscosity (h00) were studied to determine zero shear-rate viscosity (h0) and thermal activation energy Ea. Master curves were built and the shift factor aT was determined. Thermal activation energies were extracted from an Arrhenius model on the shift factor temperature’s dependency. Finally, Ea and h0 were determined thanks to the dynamic viscosity fit with Cross model and Cole–Cole representation
Fichier principal
Vignette du fichier
Coulson_20885.pdf (539.2 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01962058 , version 1 (20-12-2018)

Identifiants

Citer

Mike Coulson, Luis Enrique Quiroga Cortes, Eric Dantras, Antoine Lonjon, Colette Lacabanne. Dynamic rheological behavior of poly(ether ketone ketone) from solid state to melt state. Journal of Applied Polymer Science, 2018, 135 (27), pp.1-7. ⟨10.1002/APP.46456⟩. ⟨hal-01962058⟩
28 Consultations
162 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More