Influence of injected interstitials on $\alpha'$ precipitation in Fe–Cr alloys under self-ion irradiation

Résumé

Depending on the particle used to irradiate Fe–Cr alloys, at the same dose and temperature, α′ precipitation may occur or not. This paper aims at explaining the origin of the absence of α′ precipitation under ion irradiation. A Fe–15at.%Cr alloy was irradiated with 2 MeV Fe2+ ions at 300°C and analysed using atom probe tomography. For the first time to our knowledge, α′ particles were observed under ion irradiation. The characterisation of the α/α′ decomposition with depth showed that injected Fe strongly reduced α′ precipitation. They might have played a major role in the absence of α′ precipitation under ion irradiation.
Fichier principal
Vignette du fichier
Tissot et al. - 2017 - Influence of injected interstitials on α′ precipit.pdf (1.8 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Loading...

Dates et versions

hal-01921664 , version 1 (29-05-2019)

Identifiants

Citer

O. Tissot, Cristelle Pareige, E. Meslin, B. Décamps, J. Henry. Influence of injected interstitials on $\alpha'$ precipitation in Fe–Cr alloys under self-ion irradiation. Mater.Res.Lett., 2016, 5 (2), pp.117-123. ⟨10.1080/21663831.2016.1230896⟩. ⟨hal-01921664⟩
112 Consultations
42 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More