Thermodynamic properties of C-S-H, C-A-S-H and M-S-H phases: Results from direct measurements and predictive modelling - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Applied Geochemistry Année : 2018

Thermodynamic properties of C-S-H, C-A-S-H and M-S-H phases: Results from direct measurements and predictive modelling

Résumé

How cement-based materials behave in storage operating conditions is important in the context of a radwaste deep geological repository. In particular, we need missing thermodynamic data for ternary and low-pH cementitious materials that have high aluminum oxide content. This work reports calorimetric measurements performed on calcium silicate hydrate (C-S-H), calcium aluminate silicate hydrate (C-A-S-H) and magnesium silicate hydrate (M-S-H) gel phases. Coupled with solubility experiments and vapor adsorption isotherms, a complete set of thermodynamic parameters for C-S-H, C-A-S-H, and M-S-H is provided. The measurements are complemented by a model predicting thermodynamic properties, which is parameterized using results from this work. Predominance diagrams allow us to confirm the relation between M-S-H and low C/S phases. The diagrams support a discussion on kinetics that may play a role in relations with other Al-and Mg-bearing phases.

Domaines

Matériaux
Fichier non déposé

Dates et versions

hal-01898399 , version 1 (18-10-2018)

Identifiants

Citer

Cédric Roosz, Philippe Vieillard, Philippe Blanc, Stéphane Gaboreau, Hélène Gailhanou, et al.. Thermodynamic properties of C-S-H, C-A-S-H and M-S-H phases: Results from direct measurements and predictive modelling. Applied Geochemistry, 2018, 92, pp.140 - 156. ⟨10.1016/j.apgeochem.2018.03.004⟩. ⟨hal-01898399⟩
129 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More