Permanent indentation characterization for low-velocity impact modelling using three-point bending test
Résumé
This paper deals with the origin of permanent indentation in composite laminates subjected to low-velocity impact. The three-point bending test is used to exhibit a non-closure of matrix crack which is assumed as a cause of permanent indentation. According to the observation at microscopic level, this non-closure of crack is produced by the blocking of debris inside matrix cracking and the formation of cusps where mixed-mode delamination occurs. A simple physicallybased law of permanent indentation, ‘‘pseudo-plasticity’’, is proposed. This law is qualitatively tested by three-point bending finite element model and is lastly applied in low-velocity impact finite element model in order to predict the permanent indentation. A comparison between low-velocity impact experiments and simulations is presented.