Effect of Pore Size and Porosity on Piezoelectric and Acoustic Properties of Pb(Zr0.53Ti0.47)O3 Ceramics - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Advances in Applied Ceramics Année : 2016

Effect of Pore Size and Porosity on Piezoelectric and Acoustic Properties of Pb(Zr0.53Ti0.47)O3 Ceramics

Résumé

We studied the effect of porosity and pore morphology on the functional properties of Pb(Zr0.53Ti0.47)O3 (PZT) ceramics for application in high frequency ultrasound transducers. By sintering a powder mixture of PZT and polymethylmetacrylate spherical particles (1.5 and 10 μm) at 1080°C, we prepared ceramics with ∼30% porosity with interconnected micrometer sized pores and with predominantly ∼8 μm spherical pores. The acoustic impedance was ∼15 MRa for both samples, which was lower than for the dense PZT. The attenuation coefficient α (at 2.25 MHz) was higher for ceramics with ∼8 μm pores (0.96 dB mm− 1 MHz− 1), in comparison to the ceramic with smaller pores (0.56 dB mm− 1 MHz− 1). The high α value enables the miniaturisation of the transducer, which is crucial for medical imaging probes. The dielectric and piezoelectric coefficients, polarisation, and strain response decreased with increased porosity and decreased pore/grain size. We suggest a possible role of pore/grain size on the switching behaviour.
Fichier non déposé

Dates et versions

hal-01814873 , version 1 (13-06-2018)

Identifiants

Citer

Tina Bakaric, Tadej Rojac, André-Pierre Abellard, Barbara Malic, Franck Levassort, et al.. Effect of Pore Size and Porosity on Piezoelectric and Acoustic Properties of Pb(Zr0.53Ti0.47)O3 Ceramics. Advances in Applied Ceramics, 2016, 115 (2), pp.66-71. ⟨10.1179/1743676115Y.0000000040⟩. ⟨hal-01814873⟩
70 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More