Fabrication andin vitro characterization of three-dimensional organic/inorganic scaffolds by robocasting - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Biomedical Materials Research Part A Année : 2007

Fabrication andin vitro characterization of three-dimensional organic/inorganic scaffolds by robocasting

Julie Russias
  • Fonction : Auteur
Eduardo Saiz
  • Fonction : Auteur
Karol Gryn
  • Fonction : Auteur
G. Liu
  • Fonction : Auteur
Ravi K. Nalla
  • Fonction : Auteur
Antoni P. Tomsia
  • Fonction : Auteur

Résumé

A key issue for the fabrication of scaffolds for tissue engineering is the development of processing techniques flexible enough to produce materials with a wide spectrum of solubility (bioresorption rates) and mechanical properties matching those of calcified tissues. These techniques must also have the capability of generating adequate porosity to further serve as a framework for cell penetration, new bone formation, and subsequent remodeling. In this study, we show how hybrid organic/inorganic scaffolds with controlled microstructures can be built using robotic assisted deposition at room temperature. Polylactide or polycaprolactone scaffolds with pore sizes ranging between 200–500 μm and hydroxyapatite contents up to 70 wt % were fabricated. Compressive tests revealed an anisotropic behavior of the scaffolds, strongly dependent on their chemical composition. The inclusion of an inorganic component increased their stiffness but they were not brittle and could be easily machined even for ceramic contents up to 70 wt %. The mechanical properties of hybrid scaffolds did not degrade significantly after 20 days in simulated body fluid. However, the stiffness of pure polylactide scaffolds increased drastically due to polymer densification. Scaffolds containing bioactive glasses were also printed. After 20 days in simulated body fluid they developed an apatite layer on their surface.
Fichier principal
Vignette du fichier
Fabrication and in vitro characterization of three‐dimensional organic:inorganic scaffolds by robocasting .pdf (2.2 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01785620 , version 1 (04-05-2018)

Identifiants

Citer

Julie Russias, Eduardo Saiz, Sylvain Deville, Karol Gryn, G. Liu, et al.. Fabrication andin vitro characterization of three-dimensional organic/inorganic scaffolds by robocasting. Journal of Biomedical Materials Research Part A, 2007, 83A (2), pp.434 - 445. ⟨10.1002/jbm.a.31237⟩. ⟨hal-01785620⟩