Effect of flake powder metallurgy on thermal conductivity of graphite flakes reinforced aluminum matrix composites - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Materials Science Année : 2018

Effect of flake powder metallurgy on thermal conductivity of graphite flakes reinforced aluminum matrix composites

Résumé

The optimization of metal–matrix composite material is linked firstly with the intrinsic properties of the matrix and the reinforcement used and secondly with the reinforcement–matrix interfacial zone and the distribution/orientation of the reinforcement inside the metal–matrix. Flake powder metallurgy was used to fabricate graphite flake reinforced aluminum matrix (Al/GF) composites fabricated by vacuum hot pressing. Two types of aluminum powders morphology were used: spherical (AlS) and flake (AlF) powders. A higher thermal conductivity in the in-plane direction of the graphite flakes was obtained for Al/GF composite materials fabricated with aluminum flake powder. In addition to a better orientation of the GF in the flake aluminum matrix, a 3D puckered surface and plane surface are formed at the Al/GF interface in, respectively, AlS/GF and AlF/GF composite materials. Due to the morphology incompatibility between the graphite flakes and the spherical powder, the damaged inner structure of GF contributes to a limited enhancement of thermal conductivity in AlS/GF composite materials.
Fichier principal
Vignette du fichier
2018-066.pdf (1.19 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01779685 , version 1 (09-05-2018)

Identifiants

Citer

Nabil Chamroune, Diaa Mereib, Florence Delange, Nathalie Caillault, Yongfeng Lu, et al.. Effect of flake powder metallurgy on thermal conductivity of graphite flakes reinforced aluminum matrix composites. Journal of Materials Science, 2018, 53 (11), pp.8180-8192. ⟨10.1007/s10853-018-2139-1⟩. ⟨hal-01779685⟩
129 Consultations
591 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More