Investigation of grain-scale surface deformation of a pure aluminum polycrystal through kinematic-thermal full-field coupling measurement - Archive ouverte HAL Accéder directement au contenu
Communication Dans Un Congrès Année : 2013

Investigation of grain-scale surface deformation of a pure aluminum polycrystal through kinematic-thermal full-field coupling measurement

Résumé

This is a study of plastic strain localization, temperature evolution, surface roughening and of the origin of these phenomena in polycrystals. First, a review on different techniques of coupled kinematic-thermal measurements is given, and the two-face set-up, after several technical improvements, was employed in our work. Thanks to this integrated optical system, the full-field strain and temperature of the aluminium oligocrystal specimen were measured simultaneously during a tensile test. And the coupled data was further proceeded by following some particular methodologies, namely the Lagrangian thermography and the crystallography-based field projection. The surface profile of the deformed specimen was measured by interferometric profilometer, which showed clearly that the specimen had been suffered a strong out-of-plane deformation during the test. This out-of-plane effect was highlighted in the temperature field as well as in the strain field, which brought considerable affections on the measurement precisions of temperature and in-plane strain. Further data analysis shows that the heterogeneity of the out-of-plane deformation is closely associated with the crystallographic structure of the material, and reveals that the grain boundaries and grain interactions during the deformation play an important role in the process of deformation, temperature and surface profile evolutions.
Fichier principal
Vignette du fichier
Wang2013.pdf (693.53 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)

Dates et versions

hal-01771063 , version 1 (23-08-2021)

Licence

Paternité

Identifiants

  • HAL Id : hal-01771063 , version 1

Citer

Xiaogang Wang, Jean-Francois Witz, Ahmed El Bartali, Philippe Dufrenoy, Eric Charkaluk. Investigation of grain-scale surface deformation of a pure aluminum polycrystal through kinematic-thermal full-field coupling measurement. 13th International Conference on Fracture (ICF13), Jun 2013, Pékin, China. ⟨hal-01771063⟩

Collections

CNRS
31 Consultations
4 Téléchargements

Partager

Gmail Facebook X LinkedIn More