In Situ and Real-Time Analysis of TEM Forces Induced by a Permanent Magnetic Field during Solidification of Al-4wt%Cu - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Materials Science Forum Année : 2014

In Situ and Real-Time Analysis of TEM Forces Induced by a Permanent Magnetic Field during Solidification of Al-4wt%Cu

Résumé

It is well known that the application of a magnetic field during the growth process can have pronounced effects on cast material structures and their properties, so that magnetic fields have been widely applied since the 1950’s. In the case of a permanent magnetic field, some recent results revealed a dual effect on the liquid metal flow. 1: the magnetic field has a selective damping action on the flow at the scale of the crucible, due to the Lorentz force; 2: the interaction of thermoelectro-magnetic (TEM) currents in the close vicinity of the solid-liquid interface with the applied magnetic field leads to the generation of electromagnetic forces, which act both on the liquid and on the solid at the scale of the microstructure. We present an experimental investigation of the TEM forces induced by a permanent magnetic field during columnar and equiaxed solidification of Al- 4wt%Cu. In situ visualization was carried out by means of synchrotron X-ray radiography, which is a method of choice for studying dynamic phenomena. It was shown that the TEM forces were at the origin of a motion of dendritic particles, perpendicular to the direction of gravity. A heuristic analysis allowed us to estimate the fluid velocities and the velocities of the solid particles, and a good agreement was achieved with the experimental data. Similar observations were also made during equiaxed growth in a temperature gradient. The in situ observation of the grain trajectories for various values of the temperature gradient demonstrated that gravity and TEM forces were the driving forces which controlled the grain motion.
Fichier non déposé

Dates et versions

hal-01728130 , version 1 (09-03-2018)

Identifiants

Citer

Henri Nguyen-Thi, Jiang Wang, Georges Salloum-Abou-Jaoude, Guillaume Reinhart, Imants Kaldre, et al.. In Situ and Real-Time Analysis of TEM Forces Induced by a Permanent Magnetic Field during Solidification of Al-4wt%Cu. Materials Science Forum, 2014, 790-791, pp.420 - 425. ⟨10.4028/www.scientific.net/MSF.790-791.420⟩. ⟨hal-01728130⟩
184 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More