Stoichiometry and particle morphology effects on the aptitude to compaction of apatitic structure powders
Résumé
Apatitic calcium phosphates powders with Ca/P molar ratio of 1.5 to 1.8 were synthesized at 25 degrees C using the neutralization method. These powders, differing by stoichiometry and particle morphology, were compacted in similar conditions. For a similar morphology of particles, compacts of the non-stoichiometric powders have better cohesion than those of the stoichiometric hydroxyapatite (Ca-10(PO4)(6)(OH)(2): Ca/P=11.67). The lacunar structure, with deficiency of calcium (Ca10-x (HPO4)(x)(PO4)(6-x)(OH)(2-x): 1.5
Origine : Fichiers produits par l'(les) auteur(s)
Loading...
IMT Mines Albi IMT Mines Albi : Connectez-vous pour contacter le contributeur
https://hal.science/hal-01718078
Soumis le : jeudi 7 novembre 2019-09:28:51
Dernière modification le : vendredi 24 mars 2023-14:53:13
Archivage à long terme le : dimanche 9 février 2020-00:49:53
Citer
Z. Hatim, Abderrahim Michrafy, M. Elassfouri, F. Abida. Stoichiometry and particle morphology effects on the aptitude to compaction of apatitic structure powders. Powder Technology, 2009, 190 (1-2, SI), pp.210-214. ⟨10.1016/j.powtec.2008.04.040⟩. ⟨hal-01718078⟩
Collections
30
Consultations
64
Téléchargements