Anisotropy development during HDPE necking studied at the microscale with in situ continuous 1D SAXS scans - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Polymer Science Part B: Polymer Physics Année : 2017

Anisotropy development during HDPE necking studied at the microscale with in situ continuous 1D SAXS scans

Résumé

Quantitative information about microstructural reorganizations which occur during mechanical solicitation is important to increase our knowledge on the rheology of semi-crystalline polymers. This point is investigated here on High Density Polyethylene through the measurement of an anisotropy index calculated from small-angle X-ray scattering (SAXS) patterns. These were obtained in situ on a coherent synchrotron beamline with a very fast scanning of the specimen under tensile test. This allows the anisotropy development of many material points which undergo different deformation paths to be followed, thanks to necking development and propagation. With this field information, the microstructural anisotropy observable is shown to have a given value at a given true strain, meaning that strain pilots the bulk topology. Results apparently departing from that premise are shown indeed to be an experimental artifact: true strains are measured on the specimen surface, necking introduces strain heterogeneities in thickness, and the SAXS technique probes the full volume producing averaging.
Fichier principal
Vignette du fichier
cSAXSPaperAndre_JPSB_PreRef.pdf (2.48 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01652805 , version 1 (30-11-2017)

Identifiants

Citer

Laurent Farge, Julien Boisse, Isabelle Bihannic, Ana Diaz, Stéphane André. Anisotropy development during HDPE necking studied at the microscale with in situ continuous 1D SAXS scans. Journal of Polymer Science Part B: Polymer Physics, 2017, 56 (2), pp.170-181. ⟨10.1002/polb.24527⟩. ⟨hal-01652805⟩
116 Consultations
210 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More