Visible thermochromism in vanadium pentoxide coatings - Archive ouverte HAL Access content directly
Journal Articles ACS Applied Materials & Interfaces Year : 2017

Visible thermochromism in vanadium pentoxide coatings

Abstract

Although di-vanadium pentoxide (V2O5) has been a candidate of extensive research for over half a century, its intrinsic thermochromism has not been reported so far. Films of V2O5 grown on silicon, glass, and metal substrates by metal organic chemical vapor deposition in this study exhibit a thermally induced perceptible color change from bright yellow to deep orange. Temperature-dependent UV− vis spectroscopy and X-ray diffraction allow the correlation between the reversible continuous red shift of the absorption and the anisotropic thermal expansion along the (001) direction, that is, perpendicular to the sheets constituting the layered structure. Furthermore, the possibility of tuning the thermochromic behavior was demonstrated via a chemical doping with chromium
Fichier principal
Vignette du fichier
Kumar_19230.pdf (527.78 Ko) Télécharger le fichier
Origin : Files produced by the author(s)
Loading...

Dates and versions

hal-01651488 , version 1 (29-11-2017)

Identifiers

Cite

Sunil Kumar, Awais Qadir, Francis Maury, Naoufal Bahlawane. Visible thermochromism in vanadium pentoxide coatings. ACS Applied Materials & Interfaces, 2017, vol. 9 (n° 25), pp. 21447-21456. ⟨10.1021/acsami.7b04484⟩. ⟨hal-01651488⟩
129 View
1971 Download

Altmetric

Share

Gmail Facebook X LinkedIn More