A NEW ROUTE FOR THE SYNTHESIS OF ALKALI POLYPHOSPHATE FROM ECONOMICAL STARTING MATERIALS: PREPARATION AND CHARACTERIZATION OF SODIUM CYCLOTRIPHOSPHATE - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Phosphorus, Sulfur, and Silicon and the Related Elements Année : 2012

A NEW ROUTE FOR THE SYNTHESIS OF ALKALI POLYPHOSPHATE FROM ECONOMICAL STARTING MATERIALS: PREPARATION AND CHARACTERIZATION OF SODIUM CYCLOTRIPHOSPHATE

Résumé

Thermal synthesis of sodium cyclotriphosphate (SCTP) - Na3P3O9 was investigated in the temperature range of 150 degrees C to 750 degrees C using sodium chloride (NaCl) and 85 wt% orthophosphoric acid (H3PO4) as economical starting materials. Reaction temperature had a crucial impact on the chloride elimination rate and the formation of SCTP. The best result was obtained at 600 degrees C with 96% of elimination of the initial chloride as hydrochloric acid and 84% of selectivity in SCTP. At lower temperatures, residual chloride contents were high. At higher temperatures (650 degrees C and 750 degrees C), SCTP was melted and transformed into glassy products.
Fichier principal
Vignette du fichier
a-new-route-for-the-synthesis-of-alkali-polyphosphate.pdf (313.38 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01634017 , version 1 (20-10-2018)

Identifiants

Citer

Doan Pham Minh, Jocelyn Ramaroson, Ange Nzihou, Patrick Sharrock, Guy Depelsenaire. A NEW ROUTE FOR THE SYNTHESIS OF ALKALI POLYPHOSPHATE FROM ECONOMICAL STARTING MATERIALS: PREPARATION AND CHARACTERIZATION OF SODIUM CYCLOTRIPHOSPHATE. Phosphorus, Sulfur, and Silicon and the Related Elements, 2012, 187 (1), p.112-120. ⟨10.1080/10426507.2011.590950⟩. ⟨hal-01634017⟩
55 Consultations
192 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More