Optical and Electrical Characterizations of Uncooled Bolometers Based on LSMO Thin Films - Archive ouverte HAL Accéder directement au contenu
Communication Dans Un Congrès Année : 2017

Optical and Electrical Characterizations of Uncooled Bolometers Based on LSMO Thin Films

Résumé

In this paper the optical and electrical characterization of a 75 × 75 µm 2 uncooled bolometers based on free-standing La0.7Sr0.3MnO3 /CaTiO3 (LSMO/CTO) thin films fabricated by micromachining of the silicon substrates is presented. R(T) curves have been compared to electro thermal simulations. Its thermal conductance was measured to be 9 × 10 −6 W·K −1 around 300 K. The optical characterization was performed by modulating the power of a 635 nm laser diode and was carried out at different bias currents and temperatures. Finally, the frequency dependence of the bolometer presented at different temperatures and at optimal current shows that both sensitive and fast uncooled bolometers can be fabricated using suspended LSMO thin films.
Fichier principal
Vignette du fichier
2017_proceedings-01-00634_Eurosensors_Nascimento.pdf (1.38 Mo) Télécharger le fichier
Origine : Fichiers éditeurs autorisés sur une archive ouverte
Loading...

Dates et versions

hal-01615527 , version 1 (12-10-2017)

Identifiants

Citer

Vanuza M Nascimento, Mario E B G N Silva, Shuang Liu, Leandro Manera, Laurence Méchin, et al.. Optical and Electrical Characterizations of Uncooled Bolometers Based on LSMO Thin Films. Eurosensors 2017, Sep 2017, Paris, France. pp.634 - 634, ⟨10.3390/proceedings1040634⟩. ⟨hal-01615527⟩
153 Consultations
138 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More