Carbonated hydroxyapatite starting from calcite and different orthophosphates under moderate hydrothermal conditions: Synthesis and surface reactivity in simulated body fluid - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Materials Research Bulletin Année : 2014

Carbonated hydroxyapatite starting from calcite and different orthophosphates under moderate hydrothermal conditions: Synthesis and surface reactivity in simulated body fluid

Résumé

The one-step synthesis of carbonated hydroxyapatite (CAP) using calcite and different orthophosphates was investigated in a closed batch reactor. Only orthophosphoric acid could lead to the complete decomposition of calcite particles, when the reaction temperature was set at 80 degrees C. On the other hand, the reaction time and the dilution of the initial calcite suspension had no significant influence on the formation of the solid products. CAP was formed as the main crystalline calcium phosphate with the carbonate content in the range of 4.2-4.6 wt.%. The thermal decarbonation of the synthesized CAP started at 750 degrees C but it was only significant at 1000 degrees C under air atmosphere. This thermal decarbonation was total at 1200 degrees C or above. All CAP samples and products following thermal treatments were found bioactive in the test using simulated body fluid (SBF) solution.
Fichier principal
Vignette du fichier
carbonated-hydroxyapatite.pdf (5.33 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01611606 , version 1 (20-10-2018)

Identifiants

Citer

Doan Pham Minh, Ange Nzihou, Patrick Sharrock. Carbonated hydroxyapatite starting from calcite and different orthophosphates under moderate hydrothermal conditions: Synthesis and surface reactivity in simulated body fluid. Materials Research Bulletin, 2014, 60, p. 292-299. ⟨10.1016/j.materresbull.2014.08.052⟩. ⟨hal-01611606⟩
45 Consultations
280 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More