Synthesis, structural, optical and morphological characterization of hematite through the precipitation method: Effect of varying the nature of the base - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Molecular Structure Année : 2017

Synthesis, structural, optical and morphological characterization of hematite through the precipitation method: Effect of varying the nature of the base

Résumé

Iron oxide (a-Fe2O3) nanoparticles were synthesized using the precipitation synthesis method focusing only on (FeCl3, 6H2O), NaOH, KOH and NH4OH as raw materials. The impact of varying the nature of the base on the crystalline phase, size and morphology of a-Fe2O3 products was explored. XRD spectra revealed that samples crystallize in the rhombohedral (hexagonal) system at 800 C.The Transmission Electron Microscopy (TEM) and Scanning Electron Microscopy (SEM) were used to detect the morphology of synthesized nanoparticles and specify their sizes. However, the Fourier Transform Infra-Red (FT-IR) spectroscopy has permitted the observation of vibration band Fe-O. Raman spectroscopy was used not only to prove that we have synthesized hematite but also to identify their phonon modes. The Thermo Gravimetric Analysis (TGA) findings allow the thermal cycle determination of samples whereas Differential Thermal Analysis (DTA) findings allow the phase transition temperature identification. Besides, the optical investigation revealed that samples have an optical gap of about 2.1 eV. Findings highlight that the nature of the agent precipitant plays a significant role in the morphology of the products and the formation of the crystalline phase. Hematite synthesis with the base NH4OH brought about much stronger, sharper and wider diffraction peaks of a- Fe2O3. The morphology of samples are spherical with a size of about 61 nm while the size of the nanoparticles of hematite which we have synthesized with NaOH and KOH is respectively of the order of 82 and 79 nm.
Fichier non déposé

Dates et versions

hal-01589798 , version 1 (19-09-2017)

Identifiants

Citer

Lassoued Abdelmajid, Saber Mohamed Lassoued, Brahim Dkhil, Gadri Abdellatif, Ammar Salah. Synthesis, structural, optical and morphological characterization of hematite through the precipitation method: Effect of varying the nature of the base. Journal of Molecular Structure, 2017, 1141 (5), pp.99-106. ⟨10.1016/j.molstruc.2017.03.077⟩. ⟨hal-01589798⟩
127 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More