The oxidation behaviour of a thermal barrier coating (TBC) system is a major concern as the growth of the thermally grown oxide (TGO) layer on the bond-coating creates stresses that greatly favour the thermal barrier spallation. To delay the loss of the thermal protection provided, research has focused on the bond-coating composition and microstructure as well as on the parameters required for a suitable pre-oxidation treatment before the deposition of the ceramic top coat. Platinum is known to enhance the oxidation/corrosion resistance of MCrAlY coatings. The effect of Pt on the oxidation behaviour of a NiCoCrAlYTa coating was assessed in this study. In addition, pre-oxidation treatments were conducted to determine if the oxidation behaviour of the modified NiCoCrAlYTa coating could be further improved.