pH induced desaggregation of highly hydrophilic amphiphilic diblock copolymers

Résumé

P(nBA20%-stat-AA80%)100-b-PAA95, an amphiphilic diblock copolymer consisting of a pure hydrophilic poly(acrylic acid) (PAA) block and a weakly hydrophobic statistical copolymer of n-butyl acrylate (nBA) and acrylic acid (AA) was prepared by ATRP. Kinetic studies revealed that the polymerization was well controlled, leading to a perfectly defined diblock copolymer both in terms of chemical composition and block lengths. This polymer was characterized in aqueous solution by means of light and neutron scattering experiments. In spite of its weak hydrophobic nature, P(nBA20%-stat-AA80%)100-b-PAA95 self-assembles in aqueous solution provided the ionization degree of the AA units is kept as low as α = 0-10%. Moreover, the relatively large aggregates (Nagg = 100, Rh = 18nm) formed at α = 0% molecularly dissolve at α > 20%. This pH sensitivity is in strong contrast with the behavior of the more hydrophobic PnBA90-b-PAA100 which forms frozen aggregates insensitive to external stimuli in aqueous solution. © Springer-Verlag Berlin Heidelberg 2011.

Domaines

Polymères

Dates et versions

hal-01567839 , version 1 (24-07-2017)

Identifiants

Citer

Elise Deniau-Lejeune, C. Chassenieux, O. Colombani. pH induced desaggregation of highly hydrophilic amphiphilic diblock copolymers. Progress in Colloid and Polymer Science, 2010, 138, pp.7-16. ⟨10.1007/978-3-642-19038-4_2⟩. ⟨hal-01567839⟩

Collections

CNRS UNIV-LEMANS
43 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More