Effect of temperature on the synthesis of nanoporous carbon from copper/carbon thin films to nanoporous carbon for sensing applications - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Thin Solid Films Année : 2017

Effect of temperature on the synthesis of nanoporous carbon from copper/carbon thin films to nanoporous carbon for sensing applications

Résumé

Over the last few years, a broad panel of carbon materials was proposed for sensing applications. Among these materials, nanoporous carbon (np-C) is of particular interest due to its high specific surface area and low fabrication cost. In this contribution, the synthesis of np-C thin films using an approach combining the growth of copper/carbon nanocomposite thin films by co-sputtering followed by a selective wet etching of copper in nitric acid is studied. By adjusting the deposition conditions (e.g., powers applied to the sputtering targets, deposition temperature) of the nanocomposite thin films, it is shown that the pore size and the structure of the carbon skeleton can be modified. Furthermore, the possibility of integrating such nanoporous materials in field effect transistors for sensing application is also demonstrated.
Fichier principal
Vignette du fichier
Effect of temperature on the synthesis of nanoporous carbon_accepted.pdf (1.64 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01518057 , version 1 (04-05-2017)

Identifiants

Citer

Laëtitia Donero, Nicolas Bouts, Abdel-Aziz El Mel, Brice Le Borgne, Eric Gautron, et al.. Effect of temperature on the synthesis of nanoporous carbon from copper/carbon thin films to nanoporous carbon for sensing applications. Thin Solid Films, 2017, 630, pp.59-65. ⟨10.1016/j.tsf.2016.10.014⟩. ⟨hal-01518057⟩
110 Consultations
214 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More