Impurity-Governed Modification of Optical and Structural Properties of ZrO 2 -Based Composites Doped with Cu and Y
Résumé
The influence of calcination temperature on copper spatial localization in Y-stabilized ZrO 2 powders was studied by attenuated total reflection, diffuse reflectance, electron paramagnetic resonance, transmission electron microscopy, electron energy loss, and energy-dispersive X-ray spectroscopies. It was found that calcination temperature rise in the range of 500–700 °C caused the increase of copper concentration in the volume of ZrO 2 nanocrystals. This increase was due to Cu in-diffusion from surface complexes that contained copper ions linked with either water molecules or OH groups. This copper in-diffusion led also to an enhancement of absorption band peaked at ~270 nm that was ascribed to the formation of additional oxygen vacancies in nanocrystal volume. Further increasing of calcination temperature from 800 up to 1000 °C resulted in outward Cu diffusion accompanied by a decrease of the intensity of the 270-nm absorption band (i.e., oxygen vacancies' number), the transformation of ZrO 2 tetragonal (cubic) phase to monoclinic one as well as the enhancement of absorption band of dispersed and crystalline CuO in the 600–900 nm range.
Fichier principal
art_10.1186_s11671-017-1920-4Nano Res Lett Larysa.pdf (2.08 Mo)
Télécharger le fichier
Origine | Fichiers éditeurs autorisés sur une archive ouverte |
---|
Loading...