Mechanical behavior of amorphous PEEK in the rubbery state

Résumé

The mechanical behavior of amorphous poly(etheretherketone) (PEEK) was investigated just above the glass-transition temperature (Tg). In the rubbery state, the mobility of the macromolecular chains reveals a drop of mechanical properties with the onset of cold-crystallization as limit, as shown by dynamic-mechanical and thermal analysis. For an isothermal at 155°C, the onset of cold-crystallization begins after 40 minutes, this delay is long enough to perform static mechanical analysis. Thus, the understanding of the mechanical behavior was thoroughly investigated. From this study, different contributions are highlighted in the rubbery state: viscous and elastoplastic.
Fichier principal
Vignette du fichier
Martineau_17561.pdf (766.88 Ko) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01515536 , version 1 (27-04-2017)

Identifiants

  • HAL Id : hal-01515536 , version 1
  • OATAO : 17561

Citer

Lilian Martineau, France Chabert, Gérard Bernhart, Toufik Djilali. Mechanical behavior of amorphous PEEK in the rubbery state. ECCM17 - 17th European Conference on Composite Materials, Jun 2016, Munich, Germany. 8 p. ⟨hal-01515536⟩
273 Consultations
605 Téléchargements

Partager

Gmail Facebook X LinkedIn More