Pyroelectricity of Pb(Zr0.52Ti0.48)O3 films grown by sol-gel process on silicon

Résumé

Pyroelectric Pb(Zr0.52Ti0.48)O3 films have been grown by sol–gel process on Si(001). Intrinsic pyroelectric coefficient has been measured through ferroelectric loops recorded at different temperatures and is about −300 μC/m2K. Corresponding converted pyroelectric power density is estimated to be ~1mW/cm3 for a temperature variation of 10 °C every 6 s. Pyroelectric response of these films has been confirmed by direct measurements of the pyroelectric current with temperature variations at zero electric field. These results are of high interest for integrated thermally-sensitive devices.
Fichier non déposé

Dates et versions

hal-01489144 , version 1 (14-03-2017)

Identifiants

Citer

Rahma Moalla, G. Le Rhun, E. Defay, Nicolas Baboux, G. Sebald, et al.. Pyroelectricity of Pb(Zr0.52Ti0.48)O3 films grown by sol-gel process on silicon. Thin Solid Films, 2016, 601, pp.80. ⟨10.1016/j.tsf.2015.10.073⟩. ⟨hal-01489144⟩
179 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More