In-depth analysis of ITER-like samples composition using laser-induced breakdown spectroscopy

Résumé

Laser-induced breakdown spectroscopic in-depth measurements were undertaken for two ITER-like calibrated multi-layered samples made of W-Mo or W/C layers on Ti-substrates. The samples were previously characterized by glow discharge optical emission spectroscopy. For laser-induced breakdown spectroscopic measurements, pulses generated by Nd:YAG laser sources with 1064 nm, 532 nm, 355 nm and 266 nm wavelengths were applied. The effects of laser beam shaping, fluence and wavelength as well as the gas nature (air, Ar, He) and pressure were investigated. The results obtained with laser-induced breakdown spectroscopic in-depth measurements were compared to those obtained with glow discharge optical emission spectroscopy and found to be in agreement. However, a mixing of the layers was observed and attributed to diffusion through the melted material and to the non-homogeneity of the laser beam spatial distribution. The depth resolution was found of the order of several thermal diffusion lengths but should be improved by using picosecond laser pulse duration. The results promote applications to tritium concentration measurements with depth resolution in the deposited layers of Tokamak first walls, as in the case of the future fusion reactor ITER. (C) 2011 Elsevier B.V. All rights reserved.

Dates et versions

hal-01418624 , version 1 (16-12-2016)

Identifiants

Citer

L. Mercadier, A. Semerok, P. A. Kizub, A. V. Leontyev, J. Hermann, et al.. In-depth analysis of ITER-like samples composition using laser-induced breakdown spectroscopy. Journal of Nuclear Materials, 2011, 414 (3), pp.485-491. ⟨10.1016/j.jnucmat.2011.05.030⟩. ⟨hal-01418624⟩
75 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More