Article Dans Une Revue ACS Applied Materials & Interfaces Année : 2016

Flexible Photodiodes Based on Nitride Core/Shell p-n Junction Nanowires

Catherine Bougerol
Maria Tchernycheva

Résumé

A flexible nitride p-n photodiode is demonstrated. The device consists of a composite nanowire/polymer membrane trans- ferred onto a flexible substrate. The active element for light sensing is a vertical array of core/shell p−n junction nanowires containing InGaN/ GaN quantum wells grown by MOVPE. Electron/hole generation and transport in core/shell nanowires are modeled within nonequilibrium Green function formalism showing a good agreement with experimental results. Fully flexible transparent contacts based on a silver nanowire network are used for device fabrication, which allows bending the detector to a few millimeter curvature radius without damage. The detector shows a photoresponse at wavelengths shorter than 430 nm with a peak responsivity of 0.096 A/W at 370 nm under zero bias. The operation speed for a 0.3 × 0.3 cm2 detector patch was tested between 4 Hz and 2 kHz. The −3 dB cutoff was found to be ∼35 Hz, which is faster than the operation speed for typical photoconductive detectors and which is compatible with UV monitoring applications.
Fichier principal
Vignette du fichier
HAL Flexible photodetector ACS_revised.pdf (4.33 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01390933 , version 1 (02-11-2016)

Identifiants

Citer

H Zhang, Xing Dai, Nan Guan, Agnes Messanvi, Vladimir Neplokh, et al.. Flexible Photodiodes Based on Nitride Core/Shell p-n Junction Nanowires. ACS Applied Materials & Interfaces, 2016, 8, pp.26198 - 26206. ⟨10.1021/acsami.6b06414⟩. ⟨hal-01390933⟩
737 Consultations
159 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More