Comparative analysis of Cr-B coatings deposited by magnetron sputtering in DC and HIPIMS modes

Résumé

Surface coatings of the Cr-B system have been obtained by magnetron sputtering in the DC and high-power impulse (HIPIMS) regimes. It is established that the passage from the DC regime to HIPIMS leads to suppression of the columnar grain growth and a twofold increase in the resistance of coatings to plastic deformation, while the plasticity index and hardness of coatings increase by 29 and 18%, respectively.
Fichier non déposé

Dates et versions

hal-01293266 , version 1 (24-03-2016)

Identifiants

Citer

Ph. V. Kiryukhantsev-Korneev, David Horwat, Jean-François Pierson, E. A. Levashov. Comparative analysis of Cr-B coatings deposited by magnetron sputtering in DC and HIPIMS modes. Pis'ma v Zhurnal Tekhnicheskoi Fiziki / Technical Physics Letters, 2014, 40 (7), pp.614-617. ⟨10.1134/S1063785014070219⟩. ⟨hal-01293266⟩
26 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More