Ultraporous nanocrystalline TiO2-based films: synthesis, patterning and application as anti-reflective, self-cleaning, superhydrophilic coatings
Résumé
Crack-free, anatase-based optical coatings with a refractive index down to 1.27, a porosity up to 80 vol%, and a tunable thickness up to 1.5 mu m were fabricated. The extraordinary stability of the porosity upon thermally induced crystallisation and template removal was attributed to the combined effects of the presence of 10% molar silica in the inorganic phase, a flash treatment at 500 degrees C, and the use of templates with different dimensions ranging from a few nanometers to 50 nm. The hierarchical porous system was directly patterned by UV lithography and used as multifunctional anti-reflective, self-cleaning coatings.