Protective Coatings for Niobium Alloys: Manufacture, Characterization and Oxidation Behaviour of (TiXCr)(7)Si-6 with X = Fe, Co and Ni - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Oxidation of Metals Année : 2013

Protective Coatings for Niobium Alloys: Manufacture, Characterization and Oxidation Behaviour of (TiXCr)(7)Si-6 with X = Fe, Co and Ni

Leo Portebois
Stephane Mathieu
Lionel Aranda
Michel Vilasi

Résumé

Intermetallic single phases (TiXCr)(7)Si-6 (with X = Fe, Co or Ni) were manufactured by uniaxial hot pressing. Their full characterization (SEM + XRD) highlighted that the nature of the metal constituent X influenced the chromium content in the silicide compositions. Both isothermal and cyclic oxidation studies at a temperature as high as 1300 A degrees C evidenced very low degradation rate for all compounds and lifetime at 1100 A degrees C exceeded 4700 cycles. All phases developed a duplex protective layer of chromia and silica. It was observed that the chromia:silica ratio depended on the nature of X, and, particularly for the Ni-containing specimen, also on the temperature. Co- and Ni-containing specimens developed pure chromia during oxidation whereas Fe ones develop (CrxFe1-x)(2)O-3, reducing drastically the CrO3 volatilization during exposure at temperature higher than 1000 A degrees C.

Dates et versions

hal-01289982 , version 1 (17-03-2016)

Identifiants

Citer

Leo Portebois, Stephane Mathieu, Stephane Knittel, Lionel Aranda, Michel Vilasi. Protective Coatings for Niobium Alloys: Manufacture, Characterization and Oxidation Behaviour of (TiXCr)(7)Si-6 with X = Fe, Co and Ni. Oxidation of Metals, 2013, 80 (3-4, SI), pp.243-255. ⟨10.1007/s11085-013-9376-0⟩. ⟨hal-01289982⟩
47 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More