Evaluation of Elastic and Plastic Properties of Ni50Al50(at. (%)) and (Ni-40,Pt-10)Al-50(at. %) Single Crystals Oriented by Means of Scanning Acoustic Microscopy and Depth Sensing Indentation - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Applied Mechanics Année : 2014

Evaluation of Elastic and Plastic Properties of Ni50Al50(at. (%)) and (Ni-40,Pt-10)Al-50(at. %) Single Crystals Oriented by Means of Scanning Acoustic Microscopy and Depth Sensing Indentation

Franck Cleymand
C. J. F. Kahn
Zoubir Ayadi

Résumé

Scanning acoustic microscopy and depth sensing indentation are two techniques used for extracting Young's, shear, and indentation moduli as well as the hardness of materials. In this work, we have applied these techniques on Ni50Al50(at. %) and (Ni-40,Pt-10)Al-50(at. %) single crystals oriented (1 0 0) and (1 1 1) to measure their Young's modulus by two different techniques of local measurement and also the hardness of these alloys. Quantitative measurements highlight that the addition of 10 at.% of platinum induces a 5% decrease of Young's modulus (from 195 to 184 GPa) homogeneously spread over the surface orientations investigated, an 8% decrease of the indentation modulus, and a 40% increase of hardness without orientation effect.
Fichier non déposé

Dates et versions

hal-01273459 , version 1 (12-02-2016)

Identifiants

Citer

Franck Cleymand, A. Villemiane, Elmira Arab-Tehrany, C. J. F. Kahn, Zoubir Ayadi. Evaluation of Elastic and Plastic Properties of Ni50Al50(at. (%)) and (Ni-40,Pt-10)Al-50(at. %) Single Crystals Oriented by Means of Scanning Acoustic Microscopy and Depth Sensing Indentation. Journal of Applied Mechanics, 2014, 81 (3), ⟨10.1115/1.4024696⟩. ⟨hal-01273459⟩
144 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More