SiNx:Tb3+–Yb3+, an efficient down-conversion layer compatible with a silicon solar cell process

Résumé

SiN x : Tb 3+-Yb 3+ , an efficient down-conversion layer compatible with silicon solar cell process Abstract Tb 3+-Yb 3+ co-doped SiN x down-conversion layers compatible with silicon Photovoltaic Technology were prepared by reactive magnetron co-sputtering. Efficient sensitization of Tb 3+ ions through a SiN x host matrix and cooperative energy transfer between Tb 3+ and Yb 3+ ions were evidenced as driving mechanisms of the down-conversion process. In this paper, the film composition and microstructure are investigated alongside their optical properties, with the aim of maximizing the rare earth ions incorporation and emission efficiency. An optimized layer achieving the highest Yb 3+ emission intensity was obtained by reactive magnetron co-sputtering in a nitride rich atmosphere for 1.2 W/cm² and 0.15 W/cm² power density applied on the Tb and Yb targets, respectively. It was determined that depositing at 200 °C and annealing at 850 °C leads to comparable Yb 3+ emission intensity than depositing at 500 °C and annealing at 600 °C, which is promising for applications toward silicon solar cells.
Fichier principal
Vignette du fichier
Manuscript_free-access.pdf (1.25 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01228774 , version 1 (13-11-2015)

Licence

Paternité - Pas d'utilisation commerciale - Pas de modification

Identifiants

Citer

Lucile Dumont, Julien Cardin, Patrizio Benzo, Marzia Carrada, Christophe Labbe, et al.. SiNx:Tb3+–Yb3+, an efficient down-conversion layer compatible with a silicon solar cell process. Solar Energy Materials and Solar Cells, 2016, 145 (2), ⟨10.1016/j.solmat.2015.09.031⟩. ⟨hal-01228774⟩
2042 Consultations
184 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More