Morphological and Mechanical Properties of Hydroxyapatite Bilayer Coatings Deposited on 316L SS by Sol–Gel Method - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Metallurgical and Materials Transactions B Année : 2015

Morphological and Mechanical Properties of Hydroxyapatite Bilayer Coatings Deposited on 316L SS by Sol–Gel Method

Résumé

The present paper reports on the influence of the addition of TiO2 and SiO2 oxides as sub-layer, on the morphological and mechanical properties of the hydroxyapatite (HAP) bioceramic coatings deposited on 316L stainless steel by sol–gel method in order to improve the properties of hydroxyapatite and expand its clinical application. The stability of the sols suspensions was evaluated by measuring the time dependence of the viscosity. Annealed properties of the coatings were analyzed by XPS, XRD, SEM, and EDS. The Vickers microhardness of the coatings is obtained under the same indentation load of 10 g. The hydroxyapatite coating deposited on the surface of the 316L SS substrate exhibits a porous carbonated apatitic structure. The results clearly demonstrate that HAP-TiO2 and HAP-SiO2 bilayer coatings where hydroxyapatite is deposited on the surface of TiO2- and SiO2-coated 316L SS substrate systems were highly homogeneous and uniform and show higher microhardness compared to HAP-coated 316L SS. A gap of nearly 10 pct is observed. The addition of TiO2 and SiO2 as sub-layer of a hydroxyapatite coating results in changes in surface morphology as well as an increase of the microhardness.
Fichier non déposé

Dates et versions

hal-01206292 , version 1 (28-09-2015)

Identifiants

Citer

Djahida Sidane, Hafit Khireddine, Sabeha Yala, Salima Ziani, Fatima Bir, et al.. Morphological and Mechanical Properties of Hydroxyapatite Bilayer Coatings Deposited on 316L SS by Sol–Gel Method. Metallurgical and Materials Transactions B, 2015, 46 (5), pp.2340-2347. ⟨10.1007/s11663-015-0397-8⟩. ⟨hal-01206292⟩

Collections

CNRS
55 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More