Effect of Multi-Scale Thermoelectric Magnetic Convection on Solidification Microstructure in Directionally Solidified Al-Si Alloys Under a Transverse Magnetic Field - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Metallurgical and Materials Transactions A Année : 2014

Effect of Multi-Scale Thermoelectric Magnetic Convection on Solidification Microstructure in Directionally Solidified Al-Si Alloys Under a Transverse Magnetic Field

Résumé

The influence of a transverse magnetic field (B < 1 T) on the solidification structure in directionally solidified Al-Si alloys was investigated. Experimental results indicate that the magnetic field caused macrosegregation, dendrite refinement, and a decrease in the length of the mushy zone in both Al-7 wt pct Si alloy and Al-7 wt pct Si-1 wt pct Fe alloys. Moreover, the application of the magnetic field is capable of separating the Fe-rich intermetallic phases from Al-7 wt pct Si-1 wt pct Fe alloy. Thermoelectric magnetic convection (TEMC) was numerically simulated during the directional solidification of Al-Si alloys. The results reveal that the TEMC increases to a maximum () when the magnetic field reaches a critical magnetic field strength (), and then decreases as the magnetic field strength increases further. The TEMC exhibits the multi-scales effects: the and values are different at various scales, with decreasing and increasing as the scale decreases. The modification of the solidification structure under the magnetic field should be attributed to the TEMC on the sample and dendrite scales.

Domaines

Matériaux
Fichier non déposé

Dates et versions

hal-01120077 , version 1 (24-02-2015)

Identifiants

Citer

Xiaojian Li, D. Du, A. Gagnoud, Zhuoxiang Ren, Y. Fautrelle, et al.. Effect of Multi-Scale Thermoelectric Magnetic Convection on Solidification Microstructure in Directionally Solidified Al-Si Alloys Under a Transverse Magnetic Field. Metallurgical and Materials Transactions A, 2014, 45 (12), ⟨10.1007/s11661-014-2496-6⟩. ⟨hal-01120077⟩
54 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More