Elaboration of controlled size Li1.5Al0.5Ge1.5(PO4)3 crystallites - Archive ouverte HAL
Article Dans Une Revue Solid State Ionics Année : 2014

Elaboration of controlled size Li1.5Al0.5Ge1.5(PO4)3 crystallites

Résumé

This work concerns the elaboration and the characterization of Li1.5Al0.5Ge1.5(PO4)3 (LAGP), to be used as solid electrolyte and ionic conductor additive in composite electrodes of all-solid-state lithium-ion batteries.Large batches of LAGP powders with controlled grain size are prepared by crystallization of the corresponding glass precursor. The influence of different thermal treatments on the nucleation/growth of the crystallites was studied. Optimized crystallization of the glass during thermal treatment is obtained using ground glass.The resulting powder is pelletized by SPS technique before undergoing conductivity measurements. The grain conductivity of the SPS pellet presenting a compactness of 87% corresponds to 1.33 × 10− 4 S·cm− 1 at 20 °C, with an activation energy of 0.38 eV. The conductivities of the SPS pellets and of glass-ceramics are compared.

Domaines

Matériaux
Fichier non déposé

Dates et versions

hal-01085962 , version 1 (21-11-2014)

Identifiants

Citer

Agnieszka Kubanska, Laurence Tortet, Oliver Schäf, Laurent Castro, Michaël Dollé, et al.. Elaboration of controlled size Li1.5Al0.5Ge1.5(PO4)3 crystallites. Solid State Ionics, 2014, 266, pp.44-50. ⟨10.1016/j.ssi.2014.07.013⟩. ⟨hal-01085962⟩
174 Consultations
0 Téléchargements

Altmetric

Partager

More