Fatigue behavior of a structural steel coated with a WC-10Co-4Cr/Colmonoy 88 deposit by HVOF thermal spraying

Résumé

The fatigue behavior of a SAE 4340 steel, coated with a 50% WC-10Co-4Cr/50% Colmonoy 88 deposit, by high velocity oxygen fuel (HVOF) thermal spray, has been investigated. The change in the maximum alternating stress with the number of cycles to fracture has been described by means of the relationship advanced by Stromeyer. A fractographic analysis has been carried out on some representative fracture surfaces, by means of scanning electron microscopy (SEM) techniques. The mechanical properties of the coating were characterized by means of nanoindentation tests. The results indicate that the coating is highly heterogeneous. Its deposition gives rise to a decrease in the fatigue strength of the substrate of ∼ 30%, in comparison with the uncoated substrate. The decrease in fatigue strength is due to the presence of stress concentrators at the substrate-coating interface, as well as the intrinsic characteristics of the coating.

Domaines

Matériaux
Fichier principal
Vignette du fichier
LML_surfcoat_IOST_2012.pdf (2.22 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-01070169 , version 1 (10-10-2017)

Identifiants

Citer

José Gregorio La Barbera-Sosa, Y.Y. Santana, C. Villalobos-Gutierrez, D. Chicot, J. Lesage, et al.. Fatigue behavior of a structural steel coated with a WC-10Co-4Cr/Colmonoy 88 deposit by HVOF thermal spraying. Surface and Coatings Technology, 2013, 220, pp.248-256. ⟨10.1016/j.surfcoat.2012.05.098⟩. ⟨hal-01070169⟩

Collections

CNRS
67 Consultations
122 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More