The structural properties of GaN/AlN core-shell nanocolumn heterostructures
Résumé
The growth and structural properties of GaN/AlN core-shell nanowire heterostructures have been studied using a combination of resonant x-ray diffraction, Raman spectroscopy and high resolution transmission electron microscopy experiments. For a GaN core of 20 nm diameter on average surrounded by a homogeneous AlN shell, the built-in strain in GaN is found to agree with theoretical calculations performed using a valence force field model. It is then concluded that for an AlN thickness up to at least 12 nm both core and shell are in elastic equilibrium. However, in the case of an inhomogeneous growth of the AlN shell caused by the presence of steps on the sides of the GaN core, plastic relaxation is found to occur. Consistent with the presence of dislocations at the GaN/AlN interface, it is proposed that this plastic relaxation, especially efficient for AlN shell thickness above 3 nm, is promoted by the shear strain induced by the AlN inhomogeneity.