Thermodynamic description of the Mn-Si system: an experimental and theoretical work

Résumé

Differential thermal analyses are performed on Mn-Si alloys with xSi = 0.6206 to 0.6364. Existence of a solid solution on the MnSix (with x around 0.63) phase is evidenced. Based on a careful review of the literature, the Mn-Si system is modeled using the Calphad method. The liquid, cbcc_a12, cub_a13, fcc_a1 and bcc_a2 phases are modeled as substitution solutions using the Redlich-Kister formalism. Mn3Si, Mn5Si3 and MnSi are treated as stoichiometric compounds and the stoichiometric variations of R-Mn6Si, nu-Mn9Si2 and MnSix are respectively described as (Mn)0.49(Mn,Si)0.36(Mn,Si,VA)0.15, (Mn)0.613(Mn,Si)0.215(Mn,Si)0.108(Si)0.064 and (Mn)0.146(Mn,VA)0.220(Mn,Si)0.244(Si)0.390. The results are in good agreement with the set of experimental data which is carefully selected. Finally, a few experimental data which could be checked are suggested.

Domaines

Matériaux
Fichier non déposé

Dates et versions

hal-01063529 , version 1 (12-09-2014)

Identifiants

Citer

Alexandre Berche, Elodie Ruiz-Theron, Jean-Claude Tedenac, Rose-Marie Ayral, Florence Rouessac, et al.. Thermodynamic description of the Mn-Si system: an experimental and theoretical work. Journal of Alloys and Compounds, 2014, 615, pp.693-702. ⟨10.1016/j.jallcom.2014.06.202⟩. ⟨hal-01063529⟩
179 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More