3D structural characterisation, deformation measurements and assessment of low-density wood fibreboard under compression. The use of X-ray microtomography. - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Composites Science and Technology Année : 2008

3D structural characterisation, deformation measurements and assessment of low-density wood fibreboard under compression. The use of X-ray microtomography.

Résumé

A low-density wood fibreboard has been compressed along its transversal direction. The experiment was carried out in ESRF synchrotron (ID19) and X-ray microtomographic images were recorded for each state. Stipulating that the fibreboard is a discontinuous material essentially made of air, that the compression simply re-organises the spatial distribution of the fibres and does not involve their intrinsic mechanical properties, we are able to deduce the material points density variations along the thickness of the panel. Good agreement is achieved between the macroscopic deformation of the sample and the microscopic compression rate evaluation. Then, the modifications of structural parameters are investigated by 3D image analysis. The relationship between the local structure and the behaviour of the wood fibreboard are deduced. Finally, a modelling approach allows the local densification to be predicted and confirms the initial hypotheses about the local behaviour of the material. In particular, polyester bonds are not involved. (c) 2008 Elsevier Ltd. All rights reserved.
Fichier principal
Vignette du fichier
CSTE_2008_HAL.pdf (1.14 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00964861 , version 1 (18-02-2019)

Identifiants

Citer

Eric Badel, Christine C. Delisee, Jérôme J. Lux. 3D structural characterisation, deformation measurements and assessment of low-density wood fibreboard under compression. The use of X-ray microtomography.. Composites Science and Technology, 2008, 68 (6-7), pp.1654-1663. ⟨10.1016/j.compscitech.2008.02.013⟩. ⟨hal-00964861⟩
52 Consultations
91 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More