Effect of the M/Co substitution on magnetocrystalline anisotropy and magnetization in SmCo5− xMx compounds (M= Ga; Al) - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Applied Physics Année : 2010

Effect of the M/Co substitution on magnetocrystalline anisotropy and magnetization in SmCo5− xMx compounds (M= Ga; Al)

Résumé

The isothermal magnetization curves were carried out on magnetically aligned powder of the SmCo4Ga and SmCo4Al samples; they have been measured at 4.2 K in applied field up to 33 T produced by a water-cooled resistive magnet. The intrinsic magnetic properties such as saturation magnetization, anisotropy constant, and anisotropy field have been derived. Whereas some properties, such as the saturation magnetization or the Curie temperature are found to be strongly reduced upon Ga or Al for Co substitution, on the contrary the magnetocrystalline anisotropy is much larger for the substituted compounds. Hysteresis cycles are presented also and coercivity ranging from 4.5 to 6 T are reported. The mechanism at the origin of the coercivity is also modified from a nucleation type for SmCo5 to a pinning type for the Ga or Al containing compounds.
Fichier non déposé

Dates et versions

hal-00942105 , version 1 (04-02-2014)

Identifiants

Citer

Ancuta Laslo, Claire Colin, Olivier Isnard, M. Guillot. Effect of the M/Co substitution on magnetocrystalline anisotropy and magnetization in SmCo5− xMx compounds (M= Ga; Al). Journal of Applied Physics, 2010, 107, pp.09A732. ⟨10.1063/1.3339776⟩. ⟨hal-00942105⟩
33 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More