On the mechanical properties of TiNb based alloys

Résumé

A series of TiNb(Sn) alloys were synthesized by copper mold suction casting and subjected to different heat treatments (furnace cooling or water quenching). The microstructure, thermal and mechanical properties of the as-cast and heat treated samples were investigated. For the Ti-8.34 at.% Nb alloy, the as-cast and water quenched samples possess martensitic alpha '' phase at room temperature and compression tests of these samples show occurrence of shape memory effect. For beta phase Ti-25.57 at.% Nb alloys, stress-induced martensitic transformation was found during compression in the as-cast and water quenched samples. For the ternary Ti-25.05 at.% Nb-2.04 at.% Sn alloy, conventional linear elastic behavior was observed. It is shown that the addition of Sn increases the stability of the beta phase. The Young's moduli of these alloys were also measured by ultrasonic measurements. Water-quenched Ti-25.57 at.% Nb alloy was found to exhibit the lowest Young's modulus value. Sn addition has small impact on the Young's moduli of the TiNb alloys. (C) 2013 Elsevier B.V. All rights reserved.

Domaines

Matériaux

Dates et versions

hal-00935048 , version 1 (23-01-2014)

Identifiants

Citer

Y. Guo, K. Georgarakis, Y. Yokoyama, A.R. Yavari. On the mechanical properties of TiNb based alloys. Journal of Alloys and Compounds, 2013, 571, pp.25-30. ⟨10.1016/j.jallcom.2013.03.192⟩. ⟨hal-00935048⟩
116 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More