In boundary lubrication regime, friction reduction and antiwear processes are associated to the presence of additives in the lubricating oils or greases. These processes are due to the formation of protective tribofilms resulting from chemical reactions between the additives and the sliding surfaces, in the physico-chemical conditions of the sliding contact. Conventional antiwear additives mainly consist of transition metal organo phosphate or thiophosphates which present a remarkable efficiency in the case of contacts between ferrous alloys. In the case of non reacting surfaces, these additives become inactive. Recently developped lubrication strategies consist in the use of dispersion in oils of nano additives able to build the protective tribofilm in the sliding contact without reaction with the surfaces. Carbon fluorinated phases, due to their lamellar structure and their high chemical stability even at relatively high temperature (400°C) represent interesting candidates as lubricant nano-additives subjected to present friction reduction, anti wear and anti corrosion actions. This work presents the tribologic behaviour of some carbon fluorinated derivatives such as graphite fluorides, fluorinated carbon nanofibers, fluorinated carbon nanodiscs and fluorinated carbon blacks. The influence, on the tribologic performances, of the structure of the initial carbon phases, of the fluorination rate (0