The influence of Cu/Li ratio on precipitation in Al-Cu-Li-x alloys

Résumé

The impact of the Cu/Li ratio on the sequence and kinetics of solid-state precipitation is studied for two recently developed Al-Cu-Li-Mg-Ag alloys: AA2198 and AA2196. A quantitative evaluation of the alloy microstructure is carried out using small-angle synchrotron X-ray and neutron scattering, conventional and aberration-corrected (scanning) transmission electron microscopy and differential scanning calorimetry. It is shown that small modifications to alloy chemistry profoundly change the phases formed during natural ageing: Cu-rich clusters in the Li-lean alloy and the delta'(Al3Li) phase in the Li-rich alloy. Despite this difference in early ageing, the peak aged microstructures of the two alloys are similar, dominated by high-aspect-ratio T-1 plates with a thickness of 1.3 nm and a diameter up to 50 nm. However, the incubation time for nucleation and saturation size after growth of the precipitates is found to be significantly different between the two alloys. Small amounts of other phases from the binary Al-Cu sequence are also observed. Mechanisms of formation of the T-1 phase are discussed in view of these experimental results. (C) 2013 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Domaines

Matériaux

Dates et versions

hal-00838965 , version 1 (26-06-2013)

Identifiants

Citer

B. Decreus, A. Deschamps, F. de Geuser, P. Donnadieu, C. Sigli, et al.. The influence of Cu/Li ratio on precipitation in Al-Cu-Li-x alloys. Acta Materialia, 2013, 61 (6), pp.2207-2218. ⟨10.1016/j.actamat.2012.12.041⟩. ⟨hal-00838965⟩
128 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More