Fatigue behavior of a structural steel coated with a WC-10Co-4Cr/Colmonoy 88 deposit by HVOF thermal spraying - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Surface and Coatings Technology Année : 2013

Fatigue behavior of a structural steel coated with a WC-10Co-4Cr/Colmonoy 88 deposit by HVOF thermal spraying

Y.Y. Santana
  • Fonction : Auteur
  • PersonId : 837602
C. Villalobos-Gutierrez
  • Fonction : Auteur
Jacky Lesage
  • Fonction : Auteur
  • PersonId : 832323
Alain Iost
M.H. Staia
  • Fonction : Auteur
  • PersonId : 832337
Eli Saúl Puchi-Cabrera
  • Fonction : Auteur
  • PersonId : 957581

Résumé

The fatigue behavior of a SAE 4340 steel, coated with a 50% WC-10Co-4Cr/50% Colmonoy 88 deposit, by high velocity oxygen fuel (HVOF) thermal spray, has been investigated. The change in the maximum alternating stress with the number of cycles to fracture has been described by means of the relationship advanced by Stromeyer. A fractographic analysis has been carried out on some representative fracture surfaces, by means of scanning electron microscopy (SEM) techniques. The mechanical properties of the coating were characterized by means of nanoindentation tests. The results indicate that the coating is highly heterogeneous. Its deposition gives rise to a decrease in the fatigue strength of the substrate of ∼ 30%, in comparison with the uncoated substrate. The decrease in fatigue strength is due to the presence of stress concentrators at the substrate-coating interface, as well as the intrinsic characteristics of the coating.

Dates et versions

hal-00806941 , version 1 (02-04-2013)

Identifiants

Citer

J.G. La Barbera-Sosa, Y.Y. Santana, C. Villalobos-Gutierrez, Didier Chicot, Jacky Lesage, et al.. Fatigue behavior of a structural steel coated with a WC-10Co-4Cr/Colmonoy 88 deposit by HVOF thermal spraying. Surface and Coatings Technology, 2013, 220, pp.248-256. ⟨10.1016/j.surfcoat.2012.05.098⟩. ⟨hal-00806941⟩

Collections

CNRS
92 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More