Fabrication of acrylate monolith using photopolymerization: Effect of light intensity on electrochromatographic performance - Archive ouverte HAL Accéder directement au contenu
Article Dans Une Revue Journal of Separation Science Année : 2012

Fabrication of acrylate monolith using photopolymerization: Effect of light intensity on electrochromatographic performance

Résumé

A hexyl acrylate monolith was prepared via photopolymerization into a cyclic olefin copolymer micro-device for reversed-phase electrochromatography purposes. This work deals with the influence of the irradiation conditions (irradiation time and light intensity) used during synthesis on the electrochromatographic performances of the monolithic column obtained. Up to day, the monolith structure was often controlled by means of irradiation time at constant light intensity, but the effect of light intensity (irradiance) on the monolith structure was scarcely considered. This study shows a strong effect of light intensity on electrochromatographic efficiency. Using an optimal light intensity of 4.7 mW/cm2 and an irradiation time of a few minutes allows obtaining heights equivalent to a theoretical plate reaching down to 5 mu m for the reversed-phase separation of six polycyclic aromatic hydrocarbons.
Fichier principal
Vignette du fichier
2012 JSS-ladner-cretier-Faure Fabrication of acrylate monolith using photopolymerization.pdf (3.34 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00799846 , version 1 (23-07-2020)

Identifiants

Citer

Yoann Ladner, Gérard Crétier, Karine Faure. Fabrication of acrylate monolith using photopolymerization: Effect of light intensity on electrochromatographic performance. Journal of Separation Science, 2012, 35 (15), pp.1940-1944. ⟨10.1002/jssc.201200165⟩. ⟨hal-00799846⟩
36 Consultations
32 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More