Structural modifications of disordered YMn1-xInxO3 solid solutions evidenced by infrared and Raman spectroscopies

Résumé

Polycrystalline YMn1−xInxO3 compounds were obtained by solid state reaction and found to present a blue color for high substitution rate. X-ray diffraction analyses reveal the formation of solid solutions and the increase of cell parameters following Vegard's law. Far infrared reflectivity and Raman scattering spectra show the presence of random disorder and structural modifications without phase transition. A detailed analysis of some phonon modes allows to explain the structural changes upon doping. It was found that monocaping YO7 antiprisms are almost unaffected by substitution. However, results reveal the existence of two different MO5 (M = In, Mn) trigonal bipyramids. Their apical Mn–O distances are shorter than In–O bonds and both distances increase with the substitution rate, which is consistent with the evolution of the cell parameters.

Dates et versions

hal-00752400 , version 1 (15-11-2012)

Identifiants

Citer

M. El Amrani, V. Ta Phuoc, M.-R. Ammar, Mustapha Zaghrioui, François Gervais. Structural modifications of disordered YMn1-xInxO3 solid solutions evidenced by infrared and Raman spectroscopies. Solid State Sciences, 2012, 14, pp.1315-1320. ⟨10.1016/j.solidstatesciences.2012.06.013⟩. ⟨hal-00752400⟩
83 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More