Assessment of a new fabrication route for Fe-9Cr-1W ODS cladding tubes

Résumé

Oxide Dispersion Strengthened ferritic/martensitic steels are developed as future cladding materials for Generation IV Sodium-Cooled Fast Reactors. ODS alloys are elaborated by powder metallurgy, consolidated by hot extrusion and manufactured into tube cladding using cold rolling process. ODS steels present low ductility and high hardness at room temperature which complicate their manufacturing. Cold working leads to the hardening of the tube which needs to be softened by heat treatment. A new high temperature fabrication route performed on a Fe-9Cr-1W-Ti-Y 2O 3-ODS martensitic steel has been designed by following the hardness values, the morphological and crystallographic anisotropy and the nano-precipitation size evolution at each step of the fabrication route. Observations show that phase transformation from ferrite (α) to austenite (γ) is crucial to reduce the morphological and the crystallographic anisotropy induced by the manufacturing processes. The high temperature heat treatments permit to make the austenitic grain grow leading to an improvement of the cold workability. Ultimate Tensile Strength values obtained in the hoop direction remain about 315 MPa at 650 °C which is slightly lower compared to other Fe-9Cr ODS tubes but the new microstructure could be more favorable for creep properties.

Domaines

Matériaux
Fichier principal
Vignette du fichier
Toualbi_JNM2012.pdf (2.89 Mo) Télécharger le fichier
Origine : Fichiers produits par l'(les) auteur(s)
Loading...

Dates et versions

hal-00679120 , version 1 (21-05-2012)

Identifiants

Citer

Louise Toualbi, Cyril Cayron, Patrick Olier, Joël Malaplate, Mathilde Praud, et al.. Assessment of a new fabrication route for Fe-9Cr-1W ODS cladding tubes. Journal of Nuclear Materials, 2012, 428 (1-3), pp.47-53. ⟨10.1016/j.jnucmat.2011.12.013⟩. ⟨hal-00679120⟩
417 Consultations
827 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More