Suspended core tellurite glass optical fibers for infrared supercontinuum generation

Julien Fatome
Johann Troles
G. Renversez

Abstract

We report the fabrication and characterization of tellurite TeO(2)-ZnO-Na(2)O (TZN) microstructured suspended core optical fibers (MOFs). These fibers are designed for infrared supercontinuum generation with zero dispersion wavelength (ZDW) at 1.451 mu m. The measured losses at this wavelength are approximately 6 dB/m for a MOF with a 2.2 mu m diameter core. The effective area of a particular fiber is 3.5 mu m(2) and the nonlinear coefficient is calculated to be 437 W(-1)km(-1). By pumping a 20 cm long fiber at 1.56 mu m with a sub-nj femtosecond laser source, we generate a supercontinuum (SC) spanning over 800 nm in the 1-2 mu m wavelength range.
Fichier principal
Vignette du fichier
Savelii2011.pdf (468.75 Ko) Télécharger le fichier
Origin : Files produced by the author(s)

Dates and versions

hal-00655170 , version 1 (21-04-2021)

Licence

Attribution

Identifiers

Cite

I. Savelii, J.C. Jules, G. Gadret, B. Kibler, Julien Fatome, et al.. Suspended core tellurite glass optical fibers for infrared supercontinuum generation. Optical Materials, 2011, 33 (11), pp.1661-1666. ⟨10.1016/j.optmat.2011.05.010⟩. ⟨hal-00655170⟩
525 View
100 Download

Altmetric

Share

Gmail Facebook Twitter LinkedIn More