Perovskite oxynitride LaTiOxNy thin films : Dielectric characterization in low and high frequencies

Résumé

Lanthanum titanium oxynitride (LaTiOxNy) thin films are studied with respect to their dielectric properties in low and high frequencies. Thin films are deposited by radio frequency magnetron sputtering on different substrates. Effects of nitrogen content and crystalline quality on dielectric properties are investigated. In low-frequency range, textured LaTiOxNy thin films deposited on conductive single crystal Nb-STO show a dielectric constant ε′ ≈ 140 with low losses tanδ = 0.012 at 100 kHz. For the LaTiOxNy polycrystalline films deposited on conductive silicon substrates with platinum (Pt/Ti/SiO2/Si), the tunability reached up to 57% for a weak electric field of 50 kV/cm. In high-frequency range, epitaxial LaTiOxNy films deposited on MgO substrate present a high dielectric constant with low losses (ε′ ≈ 170, tanδ = 0.011, 12 GHz).

Domaines

Matériaux

Dates et versions

hal-00641701 , version 1 (16-11-2011)

Identifiants

Citer

Yu Lu, Ahmed Ziani, Claire Le Paven-Thivet, Ratiba Benzerga, Laurent Le Gendre, et al.. Perovskite oxynitride LaTiOxNy thin films : Dielectric characterization in low and high frequencies. Thin Solid Films, 2011, 520 (2), pp.778-783. ⟨10.1016/j.tsf.2011.01.226⟩. ⟨hal-00641701⟩
276 Consultations
0 Téléchargements

Altmetric

Partager

Gmail Facebook X LinkedIn More