Structural and electrical properties of gold nanowires/P(VDF-TrFE) nanocomposites

Résumé

High aspect ratio gold nanowires were uniformly dispersed into a P(VDF-TrFE) matrix. The nanowires were synthesized by electrodeposition using nanoporous anodic alumina oxide templates. Intrinsic optical conductivity of gold nanowires was determined by Valence Electron Energy Loss Spectroscopy. The effect of increasing volume fraction of Au nanowires on the morphology and crystallization of P(VDF-TrFE) matrix was investigated by Differential Scanning Calorimetry. The crystallinity of P(VDF-TrFE) is strongly depressed by the randomly dispersed nanowires. Above 30 vol % the crystallisation of P(VDF-TrFE) is suppressed. The bulk electrical conductivity of nanocomposite films, at room temperature, obeys a percolation behaviour at a low threshold of 2.2 vol. % and confirmed using surface resistivity value. An electrical conductivity of 100 S.m -1 is achieved for a 3 vol. % filler content.

Mots clés

Fichier principal
Vignette du fichier
PEER_stage2_10.1088%2F0022-3727%2F43%2F34%2F345401.pdf (1.61 Mo) Télécharger le fichier
Origine Fichiers produits par l'(les) auteur(s)
Licence
Loading...

Dates et versions

hal-00569688 , version 1 (25-02-2011)

Licence

Identifiants

Citer

Antoine Lonjon, Lydia Laffont, Philippe Demont, Eric Dantras, Colette Lacabanne. Structural and electrical properties of gold nanowires/P(VDF-TrFE) nanocomposites. Journal of Physics D: Applied Physics, 2010, 43 (34), pp.345401. ⟨10.1088/0022-3727/43/34/345401⟩. ⟨hal-00569688⟩
126 Consultations
366 Téléchargements

Altmetric

Partager

  • More